某高硫难处理金精矿超细磨提金试验研究

针对某高硫难处理金精矿中金大部分被黄铁矿包裹、直接氰化浸出金浸出率低的问题,采用超细磨-碱预处理-氰化浸出工艺处理金精矿,通过条件优化可获得金浸出率84.50%,氰化钠耗量控制在3 kg/t以内,该工艺简单、流程短、安全环保。     

Hydrometallurgical recovery of zinc from industrial hot dipping top ash

Top ash from hot-dip galvanizing plant was investigated as a source of secondary zinc to be returned to galvanizing bath. The waste material contained 63% Zn as metallic, oxide and hydroxychloride phases. It was leached in H₂SO₄ solutions (20% and 25%) at various bath loadings (100−300 g/L). Leaching behaviors of zinc, manganese, iron and chloride ions were investigated. A few strategies of iron elimination from leaching liquors were examined. Flocculant addition was harmful for subsequent filtration of iron precipitates due to increased viscosity of solution, while a combination of zinc oxide and calcium carbonate for rising pH resulted in the formation of dense suspension unenforceable to separate from zinc sulphate solution. Zinc electrowinning was carried out at different pH (from −0.5 to 2.8) using a range of current densities (3−10 A/dm²). Optimal conditions for pure metal recovery were: leaching in 20% H₂SO₄ solution at zinc ash content 100−150 g/L, Fe₂O₃·xH₂O precipitation using H₂O₂ and CaCO₃, zinc electrowinning at pH of 0.1−1.0 at 3−6 A/dm². Correlations between pH and free H₂SO₄ concentration in electrolyte solutions were also discussed. pH−acid concentration dependence for zinc electrolyte was between experimental and calculated curves for pure H₂SO₄ solutions, while the curve was shifted towards lower pH if ferric ions were in the solution.     

白云鄂博矿焙烧浸出-萃取沉淀分离稀土及钍的试验研究

采用焙烧浸出-萃取沉淀法从白云鄂博稀土精矿中分离稀土和钍,得到最佳焙烧浸出条件为: 矿酸比1∶1.5、焙烧时间1 h、焙烧温度200 ℃、水浸液固比8∶1、水浸时间4 h、水浸温度50 ℃,最佳条件下CeO₂、La₂O₃、Nd₂O₃、Pr₆O₁₁、Sm₂O₃和ThO₂浸出率分别为80.77%、69.24%、95.71%、76.82%、93.31% 和98.13%。采用羧酸类萃取-沉淀剂从浸液中萃取分离稀土和钍,在萃取-沉淀剂皂化度70%、料液pH=3.1、萃取-沉淀剂和钍的摩尔比4∶1的最佳条件下,稀土和钍萃取-沉淀率分别为19%和90%,实现了稀土和钍的有效分离。     

湿法炼锌酸浸渣常规干燥实验研究

本文以湿法炼锌酸性浸出渣为研究对象,实验研究干燥温度、物料量、干燥时间对酸浸渣相对脱水率的影响,综合考虑干燥工艺的时效性、经济效益以及工艺效率,控制物料量为50g、干燥温度为90℃、干燥时间为80min时,酸浸渣相对脱水率可达到98.32%。实验研究对促进酸浸渣中有价金属的资源综合利用、改善环境等具有重要的指导意义。     

柱淋滤模式下生活垃圾焚烧炉渣中Cu2+和Zn2+浸出规律

垃圾焚烧炉渣是一种活性材料，在其储存、预处理及应用等过程与雨水频繁接触时，炉渣中重金属随着水域环境发生迁移和浸出现象。本研究采用连续柱淋滤试验装置模拟自然降雨，开展了0～5mm和5～10mm焚烧炉渣的动态淋滤毒性浸出分析，重点研究了pH和降雨强度对Cu²⁺和Zn²⁺的浸出影响。结果表明，动态淋滤过程中，淋滤液pH变化对Cu²⁺和Zn²⁺的浸出水平影响显著，且在酸性较强淋滤液作用下Cu²⁺浸出水平比Zn²⁺更强，与Ⅴ类地表水环境浓度限值对比，在整个淋滤时间内Cu²⁺浸出浓度严重超标，在炉渣工程应用时需预防相关的环境风险；原生炉渣粒径大小与重金属浸出水平无直接相关性，但是0～5mm细炉渣中可浸出Zn²⁺含量更高，这与细颗粒物中Zn赋存形态和可溶出态含量较高有关；淋滤强度对重金属浸出水平影响主要反应了动态淋滤过程液固比和水分运移速率情况，当较低淋滤强度时具有低液固比，溶出液中重金属含量较高。     

云南镇源难处理金精矿工艺矿物学研究

利用X射线衍射、X射线荧光光谱（XRF）、X射线能谱分析（EDX）和矿物解离分析（MLA）等检测手段对云南镇源难处理金精矿的化学组成、矿物组成、硫化物特征以及金的分布情况进行了详细的工艺矿物学研究。结果显示：该金矿以硫化矿、碳酸盐和硅酸盐类矿物为主，含有3.18%的有机碳和2.37%的无机碳。通过金的诊断浸出发现96.16%的金被硫化物包裹，少量金以单体形式存在。通过对主要载金矿物黄铁矿、辉锑矿和毒砂的粒度、包裹及裸露情况进行分析，得出大部分硫化矿以解离单体的形式存在，少部分与其他矿物共生。根据MLA测试及金的诊断浸出，认为大部分金被硫化矿完全包裹，处理该矿石时应先进行硫化物包裹层的氧化处理，再进行金矿的浸出。     

Comprehensive recovery of the components of ferritungstite base on reductive roasting with mixed sodium salts,water leaching and magnetic separation

Ferritungstite ores have great commercial value because of the huge reserve and high content of W, Mo and Fe. But their economic recovery has long been a challenge due to its complex mineralogy and heterogeneous. The current study investigated how reductive roasting of ferritungstite ores with mixed sodium salts affected the phase evolution of W, Mo and Fe through Micro-area XRD and Powder XRD, with the goal of comprehensive transformation of ferritungstite. Reductive roasting with mixed sodium salts at 800 °C transformed ferritungstite to Na₂WO₄ and magnetite (Fe₃O₄), which were easily recovered by water leaching and magnetic separation. Furthermore, a lot of pores and gaps rather than sintering or agglomeration was observed in the ore particles after roasting by SEM-EDS, which was beneficial for the water leaching of W and Mo. As a result, 96.40% of W and 96.64% of Mo were extracted after water leaching, while an iron concentrate with an Fe content of 55.65% and recovery of 83.30% was obtained after magnetic separation. These results suggested such process would be applicable to the comprehensive recovery of valuable metals from ferritungstite ores, as well as similar tungsten ores and scraps.     

Leaching resistance of hazardous waste cement solidification after accelerated carbonation

When cement-based materials are carbonated, some of their physicochemical properties are changed, which includes reductions of porosity by 20% and pH from 12 to 13 to 8–9. These changes can enhance the retention ability of cementitious solids containing hazard waste. This research studied the effect of carbonation on the leaching resistance of hazardous waste cement solidification. The finite element software COMSOL Multiphysics was used to simulate the process of accelerated carbonation and the effect of carbonation on leaching. Laboratory tests were conducted to validate the numerical models. Parametric studies from the numerical simulations revealed that carbonation could significantly improve leaching retention capabilities of cementitious solids containing hazardous wastes.     

某铀矿搅拌浸出氧化剂替代试验研究

为解决某铀矿石酸法搅拌浸出成本居高不下的问题,探索用氯酸钠替代软锰矿作为氧化剂处理该矿石的可行性。小型、验证试验及工业应用实践表明:在适当的条件下,浸出率可达93%以上,与现有生产中以软锰矿作氧化剂的浸出率相当;此外,氯酸钠替代软锰矿并未对其他工序产生影响,且浸出成本节约了30%以上。因此,用氯酸钠作氧化剂进行常规酸法搅拌浸出处理该矿石工艺可行。     

湖北某难选金银矿选矿工艺流程试验研究

针对湖北某难选金银矿氧化率高，金、银嵌布粒度细微的性质特征，试验研究通过浮选、重选、浸出工艺等对比试验，最终确定采用全泥氰化的工艺流程回收矿石中的金、银，获得的选矿指标为：金、银的浸出率分别为68．32％、64．13％。该工艺的研究为合理开发此类金银矿提供了技术方向，同时提出了高氧化率金银矿的有效回收途径。